Common Sence

 

Heat Treatment

 

 

 

 

 

 

  • Yield Point(σs)

--------The minimum stress at which a marked increased in strain occurs without an increase in stress,

as indicated by a sharp knee in the stress-strain curve.and σs =Ps/Fo(MPa),1MPa=1N/mm2

  • Tension Strength(σb)

----------The maximum tensile stress in pound per square inch that a material is capable of sustaining,

as developed by a tension test.

  • influnce of the element in the steel

------AL powerful deoxidizer and nitride former. In small amounts, can serve as a powerful, inexpensive 

grain refiner ( i.e., restricts Austenitic grain growth ). Can improve toughness, especially  at low temperatures;

---------B,Boron reduces the brittleness of hardened steel, by having a positive influence on the transformation 

from Ferrite to Austenite to Martensite Structure. Especially on steels with lower

carbon content (e.g. C=0.27%) that tend to transform inert, Boron strongly improves 

the transformation process.

---------C,The principal element responsible for hardness in steel, due to formation 

of Fe 3C upon cooling through the Transformation Temperature, when Gamma Iron ( Austenite ) 

decomposes into Alpha Iron ( Ferrite ) + Fe3C ( Iron Carbide ). Increases tensile strength in steels. 

Ductility generally decreases as C increases, but in most cases this effect can be offset

with proper heat treatment.^ Weldability decreases as C increases. Excess oxygen usage 

may be required to remove excess C


---------Mo,Mo is a strong Carbide former and has a high effect on hardenability.  Improves control of

 heat treatment by inhibiting formation of certain microstructures ( e.g., Pearlite ). Can improves 

high temperature corrosion resistance.  Can improve toughness & fatique properties. Expensive. 

Vanadium V and Molybdenum Mo Both have influence on better toughness and have the same 

negative influence as Cr they are mostly used as fragility compensatory in High carbon steels like D2 or in

 extreme cause in  440V steel. 


----------Cr,Cr is a strong carbide former, and can improve wear resistance and somewhat

 increase resistance to softening during tempering. 

Improves hardenability depth. Promotes the response of steel containing Cr the effects of

 carburizing heat treatment. In combination with even very low P, Sn, As or Sb contents, 

Chromium and Ni-Cr alloy steels are particularly susceptible to "temper embrittlement" 

(loss of ductility when tempering or slow cooling in the range 700-1100 F). ^ When Cr > 4%, 

corrosion resistance greatly improves ( Responsible for corrosion resistance in Stainless Steels ).

 ^ Not readily oxidized from bath; requires high temperatures, increased heat time and slag volume.

----------Mn,Mn extremely reduces the critical cooling temperature und increases hardenability. Yield strength, 

tensile strength and durability increase with increasing Mn content. Also Mn has positive impact on

forging and weld ability and increases through hardening. 


----------S,P,P and S:  these elements are necessary intrusions caused by metallurgic process. They are

 undesirable and their content should be less than 0,025 %.